600g/m2 E Fiberglass Woven Roving Cloth for Reinforce and Resin
Compositing
Glass woven rovings are bidirectional fabric made by direct rovings
in plain weave pattern.
Compatible with unsaturated polyester,vinyl resin,epoxy resin.
Applicable for hand lay-up,winding and compress molding
process,suitable for manufacturing tank,boat,antomobile parts and
other FRP products.
Reinforced Fiberglass Cloth is made of high strength E glass
fiberglass yarn, with plain or twill weaving style. It is widely
used in aircraft and spaceflight industry, ship industry, chemical
industry, medical industry, military industry and sports goods,
etc. It can be used to produce golf pole, surfboard, sailboard,
boat hull, FRP tank, swimming pools, car bodies, FRP pipe as well
as other FRP products.
600g E-glass Fiberglass Woven Roving is a woven material available
in various sizes to allow custom strength, thickness, and weight in
projects. Fiberglass cloth provides great strength and durability
when layered with a resin to form a hardened composite.
Technical Specification:
| Type | Density(ends/cm) | Weight | Thickness | Width | Tensile strength (N/50*100mm) |
| Warp | Weft | (g/m²) | (mm) | (cm) | Warp | Weft |
| UPSE-8200R | 8.0 | 7.0 | 200 | 0.21 | 100 | ≥2100 | ≥2100 |
| UPSE-8250R | 7.0 | 6.0 | 255 | 0.25 | 100 | ≥2100 | ≥2100 |
| UPSE-8340R | 7.0 | 5.8 | 340 | 0.35 | 100 | ≥2500 | ≥2300 |
| UPSE-8400R | 3.6 | 3.2 | 400 | 0.40 | 100 | ≥2500 | ≥2200 |
| UPSE-8600R | 2.6 | 2.5 | 600 | 0.60 | 100 | ≥4000 | ≥3850 |
| UPSE-8800R | 1.8 | 1.8 | 800 | 0.80 | 100 | ≥4600 | ≥4400 |