Product Description
CITIC IC impact crusher spare parts impact liner
ZTIC specialized in producing wear-resist castings used in grinding
equipments and main spindle bush, brake shoe for the mill of
various specifications. It has strong casting, heat treatment and
machining ability, strict quality and process controlled methods as
well as the perfect examination and experimental means, so that can
wear-resisting products enjoy high reputation in China and sells
well all over the world.
Grinding wear parts are subjected to different combinations of
impact and abrasion, as they are used in SAG/AG, ball or rod mills.
Our wear parts are manufactured to the highest standards of
quality, traceability and delivery, ensuring high levels of
reliability for our customers. Also, our wear parts add value to
customers' processes through customized designs The use of
internationally recognized advanced specialized software simulation
mill liners for lining structure, size to optimize the design.
Barrel and cap are made of wear-resistant liner material chrome
molybdenum alloy steel, the use of convex liner, improve service
life and grinding effect.
Liner with a flat head bolts, supporting self-locking nut and
ferrule. Coupling bolts with special seals to prevent leakage of
plasma.
Quantity bolted liner wealthy amount of 5%.
Cover and cylinder liner wear-resistant rubber padding junction
strip, which is fixed by the close of the liner.
Rubber gasket between the cylinder liner and a thickness of 6mm,
noise can be reduced.
SAG/AG Mill Liners:
Integrated and/or plate and lifter designs for head and shell
liners
Grates
Pulp lifters
Filler rings
Ball Mill Liners:
Single wave liners
Modified single wave liners
Double wave liners
Shell liners
Feed head liners
Discharge end liners
Rod Mill Liners:
Shell liners
Head liners
"Wedge" shell liners
Specification for Steel Castings for Grinding Mills
Applicable Specifications
a. ASTM A609
b. ASTM A609 S1
For ASTM A 216 WCA Steel (modified):
Chemical composition |
Maximum percent allowable |
| Carbon | 0.24% ( 0.28%)
(0.28% for head and trunnion) |
| Manganese | 0.90% |
| Silicon | 0.30-0.45% |
| Sulfur | 0.025% |
| Phosphorus | 0.025% |
| Nickel | 0.25% |
| Chromium | 0.20% |
| Molybdenum | 0.15% |
| Cooper | 0.20% |
| Vanadium | 0.03% |
The intent of these modified chemical requirement is to limit the
hot tear potential in the cast steel.