1700℃ MoSi2 Heating Element

Oxidizing Atmosphere 1700℃ Molybdenum Disilicide Heating Elements

Molybdenum Disilicide Heating Elements Introduction

1. U type Molybdenum Disilicide Heating Elements is a kind of resistance heating element basically made of high pure Molybdenum Disilicide.

2. In oxidizing atmosphere, its Max temperature can reach 1800 deg.C, and its applicable temperature is 500~1700 deg.C.

3. It can be widely used in such applications as sintering and heating treating of ceramic, magnet ,glass, metallurgy ,refractory, ect.

Molybdenum Disilicide Heating Elements Technical Parameter

Following should be provided when ordering U Type MoSi2 Heating Elements:

• Grade: 1700, 1800 or 1900
• Diameter: D1/D2, mm/mm
• Heated Length: Le , mm
• Terminal length: Lu, mm
• Shank Spacing: A, mm
• Specify Le, Lu and A with the same units mm

Examples:

U-Shape, Material Grade 1800, D1=3mm, D2=6mm, Le=140mm, Lu=125mm, A=25mm

Specify as: MS18U, 3/6 x 140 x 125 x 25

Product Parameters:

1. Physical Properties of MoSi2 Heating Element

2. Chemical Properties of Physical Properties of MoSi2 Heating Element

High temperature resistance and oxidation resistance: in the oxidizing atmosphere, due to high temperature combustion, a dense quartz protective film is formed on the surface of the element to prevent further oxidation of MoSi2. When the element temperature is higher than 1700 ° C, the film melts. It is not suitable for long-term use in the temperature range of 400-700 ° C, otherwise it will be powdered due to strong oxidation at low temperature.