1850℃ MoSi2 Resistance Heating Element
1850℃ MoSi2 Resistance Heating Element Resistance Heating Element Introduction Mosi2 heating elements are a kind of resistance heating element made from Molybdenum Disilicide. It can be used in air and various gases environments. Working temperature of MoSi2 heating element is 1300C to 1800C. It has the characteristics of high temperature resistance, oxidation resistance, corrosion resistance, heating fast, long service life, high temperature low distortion, easy installation
1850℃ MoSi2 Resistance Heating Element
Resistance Heating Element Introduction
Mosi2 heating elements are a kind of resistance heating element made from Molybdenum Disilicide.
It can be used in air and various gases environments. Working temperature of MoSi2 heating
element is 1300C to 1800C. It has the characteristics of high temperature resistance, oxidation resistance, corrosion resistance, heating fast, long service life, high temperature low distortion, easy installation and maintenance, excellent chemical stability, which has been widely used as heaters in high temperature furnaces and kilns of metallurgy, glass, ceramic refractory, crystal electronic device, industrial furnace manufacture and chemical industry field.
mosi2 heating element
1. According to temperature: 1700C and 1800C
2. According to Shape: U, W, I, UL, WL, Spiral types.
mosi2 heating element standard size
(Hot zone dia / Cold zone dia)
3/6mm, 4/9mm, 6/12mm, 9/18mm, 12/24mm.
Resistance Heating Element Application
The MoSi2 Heating Elements can be widely used in such applications as sintering and heat treatment on ceramics, magnet, glass, metallurgy, refractory, etc.
Feature
- MoSi2 heating elements is a kind of resistance heating element made from Molybdenum Disilicide.
- It’s mainly used in high temperature furnaces and kilns as heaters.
- It can be used in air and various gases environments.
- Working temperature of MoSi2 heating element is 1300C to 1800C.
- Widely used in the industries of metallurgy, glass, ceramic refractory,crystal electronic device, industrial furnace manufacture, etc
Physics characters
|
Bulk density |
Bending strength |
Hardness |
Apparent porosity |
Drawing water rate |
Thermal elongation |
|
5.6~5.8g/cm3 |
20MPa(20℃) |
(hv)570kg/mm² |
0.5~2.0% |
0.5% |
4% |
Recommend surface load:
|
Furnace Temp(°c) |
1400 |
1500 |
1600 |
1650 |
1700 |
|
Surface load of hot zone(W/cm²) |
<18 |
<15 |
<12 |
<10 |
<8 |
Application:
|
Item |
name |
distinction criterion |
specification |
|
Heating elements |
1700 type |
Element operating temperature 1700℃ is acceptable |
Le Φ |
|
1800 type |
Element operating temperature 1800℃ is acceptable |
||
|
1800J type |
Element operating temperature≥1800℃ |
Le Φ |
|
|
1800T type |
Element operating temperature≤1800℃ |
Le Φ |