Elastic Two Component Colored Polyaspartic Polyurea TD-002A/B
Elastic two-component colored polyaspartic polyurea TD-002A/B Characteristics Super weather resistance, super wear resistance Crack resistance, long service life High solid content low VOC, low taste environmental protection Fast curing, easy construction, no special equipment Typical use It is used to contact the base surface of acid and alkali, and has the functions of waterproof and acid and alkali resistance. Test data Flexibility 2 Shock resistance cm 50 Adhesion
Elastic two-component colored polyaspartic polyurea TD-002A/B
Characteristics
- Super weather resistance, super wear resistance
- Crack resistance, long service life
- High solid content low VOC, low taste environmental protection
- Fast curing, easy construction, no special equipment
Typical use
It is used to contact the base surface of acid and alkali, and has the functions of waterproof and acid and alkali resistance.
Test data
| Flexibility | 2 |
| Shock resistance cm | 50 |
| Adhesion (spacing 1mm) | 1 |
| Adhesion (pulling method) Mpa | 4 |
| Acid resistance (10% hydrochloric acid 120h) | No change |
| Alkaline resistance (intrusion into 20%Na0H solution for 7 days) | No change |
Technical Index
| Serial | Project | Technical Index | Test Standard |
| 1 | Hardness (shao A) | ≤ 40 |
HG/T3831 -2006 |
| 2 | Tensile strength MPa | ≥ 10 | |
| 3 | Elongation at break % | ≥ 300 | |
| 4 |
abrasive |
≤ 40 | |
| 5 | Adhesion strength Mpa |
≥2.5(Or substrate damage) |
Basic parameter
| Component | two |
| Dry film thickness | 80-100μ m |
| Theoretical coating rate ㎡/kg | 0.2 |
| Density | 1.25 |
| The Suggested thickness | 150-180μ m |
General description of construction
| Construction method | Spray or roll coating |
| Mixing ratio Weight ratio | A:B=1:1 |
Packing
A= 10kgs B=10kgs