650°C Calcium Silicate Pipe Cover Insulation - 25mm to 90mm Thickness, 16mm to 4800mm Diameter, High Temperature Industrial Grade
White calcium silicate pipe insulation with 650°C service temperature, excellent thermal performance (≤0.060 W/m·k), and high compressive strength. Asbestos-free rigid insulation ideal for power plants, petrochemical facilities, and industrial pipeline systems. Available in multiple thicknesses from 25mm to 90mm and diameters from 16mm to 4800mm.
650°C White Calcium Silicate Pipe Cover Insulation Material is a high-temperature, asbestos-free insulation solution designed for industrial applications requiring thermal protection up to 650°C (1200°F).
| Property | Unit | TUNGKIN-200 | TUNGKIN-220 | JIS A-9510 No.2-22 | ASTM C-533 Type I | TUNGKIN-170 | JIS A-9510 No.2-17 |
|---|---|---|---|---|---|---|---|
| Density | Kg/m³ | ≤200 | ≤220 | ≤220 | ≤240 | ≤170 | ≤170 |
| Service Temperature | °C (°F) | ≤650 (≤1200) | ≤650 (≤1200) | ≤650 | ≤649 (≤1200) | ≤650 (≤1200) | ≤650 |
| Compressive Strength | MPa (kgf/cm²) | ≥0.55 (≥5.61) | ≥0.58 (≥5.92) | ≥0.414 | ≥0.51 (≥5.20) | ||
| Thermal Conductivity | W/m·k (70±5°C) | ≤0.060 | ≤0.062 | ≤0.062 | ≤0.065 | ≤0.054 | ≤0.055 |
| Moisture | % | ≤5 | ≤5 | ≤5 | |||
| Linear Shrinkage (650°C 16h) | % | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 |
| Bending Strength | MPa (kgf/cm²) | ≥0.42 (≥4.28) | ≥0.43 (≥4.38) | ≥0.3 (≥3.1) | ≥0.310 | ≥0.41 (≥4.18) | ≥0.2 (≥2.0) |
| Parameter | Available Sizes |
|---|---|
| Inside Diameter | 16mm (1/4") - 4800mm (188") |
| Length | 600mm, 610mm |
| Thickness | 25mm, 30mm, 40mm, 50mm, 60mm, 65mm, 70mm, 75mm, 80mm, 90mm |
Tungkin Calcium Silicate Pipe Insulation 650°C is a micro-porous structure insulation material manufactured from inorganic siliceous material and hydrous calcium silicate powder. This white, asbestos-free rigid insulation product provides reliable thermal protection with service temperatures up to 650°C (1200°F).
Calcium Silicate Pipe Insulation 650°C features excellent thermal performance, high service temperature capability, and superior compressive and bending strength. It is widely used in power plants, petrochemical facilities, pipeline systems, industrial equipment, and heating pipe network systems.
- Light weight construction for easy installation
- Fire resistance for enhanced safety
- High temperature performance up to 650°C
- Excellent thermal conductivity properties
- Superior mechanical strength characteristics